Main Functions of the Front-of-Furnace Molten Iron Carbon-Silicon-Manganese Rapid Analyzer

1. Determination of carbon (C%), silicon (Si%), manganese (Mn%), and carbon equivalent (CEL);

2. Prediction of tensile strength and hardness of gray cast iron;

3. Determination of tensile strength and hardness of gray cast iron molten iron after inoculation, and prediction of inoculation effect;

4. After the composition determination is completed, the system automatically calculates the adjustment amount of alloy addition based on the target values of carbon, silicon, and manganese content preset by the user;

5. Automatic saving of measurement results;

6. Historical cooling curves and historical measurement results can be reproduced at any time;

7. Measurement data can be exported to Excel for data analysis, or copied to an office computer via USB interface for storage and analysis;

8. Comes with a powerful and user-friendly ingredient calculation software.

Special Features of the Front-of-Furnace Molten Iron Carbon-Silicon-Manganese Rapid Analyzer

1. After composition determination, users can modify the target values of carbon, silicon, and manganese content according to product requirements to recalculate the adjustment amount of alloy addition, making the adjusted molten iron composition better meet product requirements.

2. Determination of tensile strength and hardness of gray cast iron molten iron after inoculation, with higher accuracy.

Technical Parameters of the Front-of-Furnace Molten Iron Carbon-Silicon-Manganese Rapid Analyzer

Analysis time: Approximately 1.5 minutes

Measurement range and measurement accuracy:

Carbon equivalent CEL: 2.50–4.80%; ±0.08%

Carbon content C%: 2.30–4.20%; ±0.05%

Silicon content Si%: 0.60–3.80%; ±0.10%

Manganese content Mn%: 0.10–1.40%; ±0.10%

Tensile strength: 100–400 MPa; ±10 MPa

Hardness: 150–300 HB; ±10 HB